2010 Solid polymer electrolytes based on crosslinkable polyoctahedral silse…
페이지 정보
본문
Abstract
Solid polymer electrolytes (SPE), based on polyoctahedral silsesquioxanes (POSS) as a crosslinking agent, were prepared by radical polymerization. The ionic conductivity is greatly enhanced by introduction of crosslinkable POSS with multifunctional groups. The SPE prepared with 5 wt.% crosslinking agent shows an ionic conductivity of 5.3 × 10−4 S cm−1 at room temperature. The content of nonvolatile plasticizer, poly(ethylene glycol) dimethyl ether, in the SPE, could be raised to 95 wt.% without any leakage. The SPE is found to be electrochemically stable up to 5.3 V. Lithium polymer cell consisting of Li/SPE/LiCoO2 exhibits 80% of initial discharge capacity even at the rate of 0.1 C at room temperature after 20 cycles, which is a substantial improvement for practical consideration of lithium polymer batteries at room temperature.
관련링크
- 이전글Effect of fluoroethylene carbonate on high temperature capacity retention of LiMn2O4/graphite Li-ion cells 24.04.17
- 다음글Separator grafted with siloxane by electron beam irradiation for lithium secondary batteries 24.04.17
댓글목록
등록된 댓글이 없습니다.